L'agente schiumogeno per calcestruzzo espanso ha un impatto estremamente critico sulla qualità del calcestruzzo espanso. L'agente schiumogeno di alta qualità può produrre calcestruzzo espanso di alta qualità. Le prestazioni dell'agente schiumogeno per calcestruzzo espanso non sono legate solo al tempo di stabilizzazione e all'uniformità della schiuma, ma anche alla dimensione della bolla e alla velocità di sanguinamento.
The foam diameter of Agente schiumogeno for Foam Concrete is not as big as possible, it should be about 1mm
The pores have the same requirements for the pore diameter, and the same should be the same for the bubble diameter. Many producers ask the foam pore size to be as small as 0.1mm. Infatti, it is because if the physical foaming has a large foam diameter, the stability of the foam is poor and foamed concrete cannot be made. Le stesse materie prime e formula, le stesse attrezzature e tecnologie, just change the bubble diameter, the compressive strength of foam concrete with 1mm bubble diameter is at least 20% higher than that of foam concrete with 0.1mm bubble diameter. Perciò, it is wrong to pursue a large bubble diameter of 0.1mm or more. It is a misunderstanding in the production of foam concrete and should be corrected.
Foaming Agent for Foam Concrete's foam bleeding rate is as low as possible, evitare l'uso di schiuma di latte
According to the size of water content, foam is divided into milky foam with more water and less foam and sponge foam with more and less water. Tra loro, milky foam is unqualified and inferior foam and cannot be used.
After the foam of the Foaming Agent for Foam Concrete is produced, it gradually oozes water. The bleeding consists of two parts:
(1) Bleeding of foam liquid film. This part of water is secreted from the liquid film, which is the water secreted by the liquid film under the combined action of gravity drainage, drenaggio della tensione superficiale, and liquid film destruction drainage. Più spesso è il film liquido della schiuma, the greater the bleeding; the faster and more the foam bursts, the greater the bleeding.
(2) Water between bubbles. This part is water with no bubble liquid film formed. The worse the foaming performance of Foaming Agent for Foam Concrete and the foaming machine, the more water between the bubbles that cannot form a foam liquid film. They are actually water that can't become bubbles.
When the bleeding rate of the foam is high, sarà sottile come il succo galleggiante, turbulent flow, can not pile up, the amount of water in the foam is very large. When this kind of foam is added to the cement slurry, l'impasto di cemento diventa molto sottile, but the foam is very small, the volume of the slurry is small, and the foamed concrete produced has a high density, which does not meet the technical requirements.
Perciò, non è possibile utilizzare la schiuma di latte. The appearance of the foam that meets the technical requirements should be spongy, fine and small bubbles, piled up like white clouds, like bounced cotton, e non scorrerà in modo casuale. The water content of this foam is very small. This shows that its foam liquid film has little bleeding, the foam is not easy to burst, c'è poca acqua tra le bolle, and the amount of bubbles is large, and most of the volume is air bubbles. What needs to be emphasized here is that the sponge foam must be small bubbles with a bubble diameter of less than 1mm, not large bubbles of a few millimeters or even tens of millimeters. Large bubbles are easy to pile up, and they look like white clouds, ma perché il diametro della bolla è troppo grande, è anche non qualificato.
The low bleeding of foam is required to ensure the number of bubbles in the foam and the porosity of the foam concrete, which is to ensure the density of the foam concrete.
The foam of Foaming Agent for Foam Concrete has no side effects on cementitious materials
Cementitious material is the main source of the strength of foam concrete. The addition of Foaming Agent for Foam Concrete cannot affect its gelation, questo è, it does not produce negative gelation effects. This cannot be achieved by all kinds of bubbles.
In long-term tests, we have found that many foams hinder the gelation of cement, magnesite and gypsum, which can reduce the strength of foamed concrete, and sometimes even the hardened concrete basically loses its strength. The stability of these foams is very good. It lasts for a few hours. It looks like a sponge, has low bleeding, and has a uniform density. It meets the technical requirements in all aspects, but it is not compatible with the gelling material, so it cannot be used in production. . This shows that foams that are qualified in other aspects, such as the impact strength, are ultimately not technical requirements.
Cie-China.org è il principale fornitore di additivi per calcestruzzo espanso che fornisce agenti schiumogeni per calcestruzzo, superfluidificante,potenziatore della resistenza del calcestruzzo espanso per calcestruzzo leggero, Blocchi CLC. Se stai cercando schiumaing agente, per favore sentitevi liberi di farlo contattaci.