Hiệu suất cao polycarboxylate water reducer with high dispersibility, good retention performance, low concrete shrinkage and strong molecular structure.In addition, the polycarboxylate water reducing agent does not use formaldehyde and other outstanding advantages in the production process, which meets the needs of modern society to promote green environmental protection. Since entering the 21st century, it has gradually replaced other types of water reducing agents, and has been widely used in concrete engineering.
Đặc biệt, the technical limitations of traditional high-efficiency water reducers such as naphthalene and aliphatic are difficult to meet the requirements of engineering concrete such as bridges, đập nước, đường hầm, và các tòa nhà cao tầng.
Vì thế, polycarboxylate water reducing agent has gradually become the preferred water reducing agent for formulating high performance concrete.
But the influence of the composition of concrete on the water reducing agent.
1.Influence of fine aggregate
In the preparation of concrete, there are two main types of fine aggregates, namely mechanical sand and natural sand.Natural sand also covers river sand, earth sand and desalinated sea sand.Fine aggregates have an impact on concrete slump and, Ngoài ra, affect concrete strength under special conditions.Other properties in the fine aggregate also have an effect on the adaptability of the concrete. Ví dụ, the specific fineness modulus of the sand, đó là, when the sand fineness modulus is relatively small, the concrete will be in a dry state, thereby reducing the concrete fluidity.
2.Cement effect
The cement itself contains relatively large amounts of water, so the performance relationship between the cement component and the polycarboxylate superplasticizer is very close.Compared with ordinary water reducing agents, polycarboxylate water reducing agents can quickly combine various components in concrete.That is, the connection with water molecules is very close, so that a large amount of water molecules are absorbed.However, the water reducing effect of the polycarboxylate superplasticizer is also affected by temperature factors.In the concrete mixing process, it is necessary to control the appropriate temperature to prevent the temperature from restricting the fluidity in the concrete raw materials, thereby failing to achieve the effect of water reduction, and also affecting the condensation effect and speed in the concrete material.
3.The effect of coarse aggregate
Under the condition that the mud content is higher than 3%, the performance of the water reducing agent can be significantly reduced. tại thời điểm này, good fluidity cannot be obtained by appropriately increasing the dosage.In the process of preparing concrete materials in the future, it is necessary to take good measures to adjust the grade of cement materials to ensure the quality of concrete materials.
4.The influence of other substances
The effects of other substances are also important. Ví dụ, blast furnace slag and fly ash are more common, which makes the adaptability of polycarboxylate superplasticizers affected. The amount of fly ash and blast furnace slag needs to be controlled within a certain range, namely 30% Và 20% tương ứng, which can well guarantee the fluidity of concrete materials.
Cie-China.org là nhà cung cấp phụ gia bê tông bọt hàng đầu cung cấp chất tạo bọt bê tông, chất siêu dẻo,Chất tăng cường cường độ bê tông bọt cho bê tông nhẹ, khối CLC. Nếu bạn đang tìm kiếm chất siêu dẻo, xin vui lòng liên hệ với chúng tôi.