Yfirlit yfir Foam Concrete

CLC brick making process

In traditional foam concrete production, the cement foaming agent is dissolved. The foam generator is used to mix the foam produced by it into the slurry composed of cementitious materials and admixtures used in concrete. The foam concrete with micropores is obtained after mixing, steypa, mótun, og lækna.

Characteristics of foam concrete

Freyða steypuþéttleiki er um 500-1200 kg/m3; varmaleiðni er almennt 0.12-0.30 W/(m·k).Þrýstistyrkurinn er almennt 3-14 MPa, og er það oft notað sem einangrunarlag fyrir þök, sjálfbærandi veggir, og hitarör. The current ultra-light foam concrete has a very low density and thermal conductivity, and its thermal performance is very excellent, such as a density of 80 kg/m3.The thermal conductivity of foamed concrete is 0.040 W/(m·k); the thermal conductivity of foamed concrete with a density of 100 kg/m3 is 0.043 W/(m·k); the thermal conductivity of foamed concrete with a thickness of 120 kg/m3 is It is 0.047 W/(m·k). Sem stendur, in the world, if the material has a low thermal conductivity, it can be called an insulation material. The thermal conductivity of high-efficiency insulation materials must be lower than 0.05 W/(m·k). Ultra-light foam concrete has been used as a high-efficiency thermal insulation material, its performance is entirely comparable to organic thermal insulation materials such as polyurethane and polystyrene, and because of its high flame retardant coefficient, long service life.

Toxic gas has now become a popularized product of building insulation materials and has begun to gradually replace organic insulation materials on the market, becoming the new favorite of the building insulation industry.

Another definition of foam concrete is: nota sement, íblöndunarefni, o.s.frv. as the primary cementing material, add water and foam concrete admixture to prepare a slurry, and then foam through the cement foaming agent, cast, lögun, and cure to make A large number of small, independent, létt froðusteypa með jafndreifðum loftbólum.

Forskrift um froðusteypu

(1) Flokkun eftir mismun á þéttleika

Varma einangrunar froðu steypu: froðusteypa aðallega notuð til varmaeinangrunar. Venjulega, það er frauðsteypa með magnþéttleika á 400 kg/m3 eða minna. Ofurlétt froðusteypa sem framleidd hefur verið á undanförnum árum hefur eiginleika skilvirkrar varmaverndar.

Burðarbær froðusteypa: Notað sem burðarefni, og hefur einnig ákveðin orkusparandi og varmaeinangrunaráhrif. Venjulega, það er magnþéttleiki.

Frauðsteypa að ofan 700 g/m3.

Burðarandi og varmavarandi froðusteypa: Notað sem sjálfbær froðusteypa. Venjulega, það er frauðsteypa með magnþéttleika á 500-600 kg/m3.

(2) Flokkun eftir mismunandi froðumyndunaraðferðum

Líkamlegt sement froðuefni: Froðuefni fyrir steypu: froðuefni fyrir steypu, sem er byggt á yfirborðsvirkum efnum, is foamed through a foam generator and mixed with a mixed slurry. The density of the foam concrete is adjusted by changing the number of bubbles. The foam concrete prepared by this method has good construction performance but is too dependent on the foaming machine.

Kemísk froðuefni froðusteypa: Use hydrogen peroxide or aluminum powder to release gas through a chemical reaction to make foam concrete. The temperature of the concrete and the consistency of the slurry will affect the foaming time and the foaming amount, sem kalla má eftirfroðumyndun.

Steinsteypa froðuð eftir blöndun: nota yfirborðsvirk efni, froðuefni sem byggir á próteinum úr dýrum og plöntum, o.s.frv. á að setja í hrærivélina,

Hrært saman við slurry, þetta er aðferð til að búa til loftbólur með því að byrja. Blöndunartími þess, blöndunarhraði, einbeiting.

Breyting á kornastærð efnisins og aðrir þættir geta stillt loftinnihaldið, og vinnanleika er aðeins hægt að ná með því að hræra.

(3) Samkvæmt mismunandi gerðum fyllinga

Pólýstýren agnir froðuð steinsteypa notar pólýstýren agnir sem fylliefni, blandaðu því saman við froðusteypu, blandið saman og hellið.

Froðusteypa er unnin með innspýtingu.

Stækkuð perlít frauðsteypa: frauðsteypa gerð með því að nota stækkað perlít sem malarefni. Að auki, það eru léttar moldar froðusteypu unnin með pólýúretan ögnum, fenól plastefni agnir, glerungar örperluagnir, og vermikúlít.

(4) Samkvæmt mismunandi flokkun framleiðsluferlisins

Verksmiðjuforsmíðað froðusteypa: vísar til froðusteypu sem er forsmíðað í sérhæfðum efnaverksmiðjum, eins og einangrunarplata úr froðusteypu,

CLC kubbar og frauðsteypu veggplötur, o.s.frv.

Útsteypa á staðnum á frauðsteypu: eins og jarðhitaeinangrunarlag, gólfhita hitaeinangrunarlag, veggyfirborðshelling og fylling í miklu magni.

Cie-China.org er leiðandi framleiðandi froðusteypuaukefna sem veitir steypufreyðiefni, ofurmýkingarefni,styrktarstyrkur froðusteypu fyrir létta steypu, CLC blokkir. Ef þú ert að leita að froðuefni, vinsamlegast ekki hika við hafðu samband við okkur.