Entschlüsseln Sie die Zementmenge in Schaumbeton

What are the raw materials of Schaumbeton?

Der Hauptbestandteil von Schaumbeton ist Zement, Flugasche, Silica-Rauch, Faser, usw. Some proportions have more cement content, and some proportions have less cement proportions, so specific problems must be analyzed in detail. Because foamed concrete is mostly cured under normal temperature conditions, und eine große Menge Schaum wird hinzugefügt, these two factors determine that its cement ratio will be higher.

What is ALC?

ALC is the abbreviation of autoclaved lightweight concrete, which is a kind of high-performance autoclaved aerated concrete (ALC). ALC board is made of fly ash (or silica sand), Zement, Kalk, usw. als Hauptrohstoffe, and is cured by high-pressure steam to form a porous concrete sheet (containing processed steel reinforcement). ALC board can be used as wall material and roof panel. It is a new type of building material with superior performance. ALC board first appeared in Europe, and Japan, Europe and other regions have more than 40 years of production and application history. Derzeit, the production technology and production equipment of domestic manufacturers are mainly imported from Japan and Germany.

Foam concrete is fundamentally different from ALC. Because ALC adopts autoclave, Es beruht hauptsächlich auf der Hydratationsreaktion von Flugasche und Kalk unter hoher Hitze und hohem Druck, um eine Gelierung zu erzeugen. Cement is an auxiliary material.

While foam concrete is produced at room temperature, the active microaggregate will not quickly produce hydration reaction, und sein fester Schaum hängt immer noch von der zementierenden Wirkung von Zement ab. daher, the mixing ratio of foamed concrete must be cement as the main body, und hoher Zementanteil.

Unter normalen Umständen, the amount of cement should account for more than 30% der Gesamtmenge an Trockenstoffen, Und 30% should be the minimum use amount for its normal temperature curing. Beim Gießen vor Ort, Der Zementanteil sollte mehr als ausmachen 60% der gesamten Trockenmasse. Für Normaltemperatur-Schaumbeton mit einer Dichte darunter 600 kg/m3, Der Zementanteil sollte nicht unterschritten werden 70% des Gesamtmaterials. Wenn die Dichte darunter liegt 400 kg/m3, the conventional proportion should account for more than 90% des gesamten Trockenmaterials.

The following factors should be considered in the design of cement ratio:

(1) The variety of cement. Zementsorten mit hoher Früh- und Spätfestigkeit (wie z. B. Dual-Fast-Portlandzement) kann den Zementanteil entsprechend reduzieren, und Zementsorten mit geringer Spätfestigkeit bzw. geringer Frühfestigkeit sollten den Zementanteil erhöhen;

(2) Strength grade of cement. High-strength grade cement (wie zum Beispiel 42.5, 52.5, usw.) can reduce the proportioning amount, und bei Zement geringer Festigkeit sollte die Dosierungsmenge erhöht werden;

(3) The quality of cement. For large plants’ new dry-process rotary kiln cement, the mixing ratio can be appropriately reduced, while for small plants, shaft kiln cement or cement with a large mixing ratio should be appropriately increased;

(4) Density and strength requirements of the product. Eine niedrige Dichte oder höhere Festigkeitsanforderungen sollten den Zementanteil erhöhen, Eine hohe Dichte oder geringere Festigkeitsanforderungen können den Zementanteil verringern;

(5) Initial growth temperature. Die anfängliche Aushärtetemperatur nach dem Gießen (gießen) ist niedriger (<25°C). The proportion of cement should be increased. When the initial curing temperature is high (25℃-45℃), the proportion of cement can be appropriately reduced. If steam curing or autoclave is used, it is still strong to reduce the proportion of cement;

(6) Variety and activity of active micro-aggregate (Beimischung). Durch den Einsatz hochaktiver Mikrozuschlagstoffe kann der Zementanteil reduziert werden (wie ultrafeine Schlacke), während der Verwendung von Mikroaggregaten mit geringer Aktivität (wie sekundäre Flugasche) kann den Zementanteil erhöhen.

Cie-China.org ist der führende Anbieter von Schaumbetonzusätzen und Betonschaummitteln, Superplastifizierer,Schaumbeton-Festigkeitsverstärker für Leichtbeton, CLC-Blöcke. Wenn Sie suchen Schaummittel, Bitte zögern Sie nicht Kontaktieren Sie uns.