What are the raw materials of пенобетонй?

The main components of foamed concrete are cement, хокистар, дуди кремний, нах, ва гайра. Some proportions have more cement content, and some proportions have less cement proportions, so specific problems must be analyzed in detail. Because foamed concrete is mostly cured under normal temperature conditions, ва ба микдори зиёд кафк андохта мешавад, these two factors determine that its cement ratio will be higher.

What is ALC?

ALC is the abbreviation of autoclaved lightweight concrete, which is a kind of high-performance autoclaved aerated concrete (ALC). ALC board is made of fly ash (or silica sand), цемент, оҳак, ва гайра. хамчун ашьёи хоми асосй, and is cured by high-pressure steam to form a porous concrete sheet (containing processed steel reinforcement). ALC board can be used as wall material and roof panel. It is a new type of building material with superior performance. ALC board first appeared in Europe, and Japan, Europe and other regions have more than 40 years of production and application history. Дар айни ҳол, the production technology and production equipment of domestic manufacturers are mainly imported from Japan and Germany.

Foam concrete is fundamentally different from ALC. Because ALC adopts autoclave, он асосан ба реаксияи гидратсияи хокистар ва оҳак дар зери гармӣ ва фишори баланд барои тавлиди гелатсия такя мекунад. Cement is an auxiliary material.

While foam concrete is produced at room temperature, the active microaggregate will not quickly produce hydration reaction, ва кафки сахти он хануз ба таъсири цементкунии цемент вобаста аст. Бинобар ин, the mixing ratio of foamed concrete must be cement as the main body, ва таносуби баланди цемент.

Дар шароити муқаррарӣ, the amount of cement should account for more than 30% аз микдори умумии масолехи хушк, ва 30% should be the minimum use amount for its normal temperature curing. Ҳангоми рехтан дар сайт, таносуби цемент бояд бештар аз 60% аз хисоби умумии масолехи хушк. Барои ҳарорати муқаррарӣ бетон кафк бо зичии поён 600 кг/м3, таносуби цемент набояд аз 70% аз ҳаҷми умумии мавод. Вақте ки зичии он дар поён аст 400 кг/м3, the conventional proportion should account for more than 90% аз ҳаҷми умумии маводи хушк.

The following factors should be considered in the design of cement ratio:

(1) The variety of cement. Навъҳои семент бо қувваи баланди барвақт ва дер (монанди портландцементи дучанд тез) метавонад ба таври бояду шояд таносуби цементро кам кунад, ва навъҳои семент, ки қавии дер дер ва ё қавии барвақт кам доранд, бояд таносуби сементро зиёд кунанд;

(2) Strength grade of cement. High-strength grade cement (ба мисли 42.5, 52.5, ва гайра.) can reduce the proportioning amount, ва цементи навъи кам-мустахкам бояд микдори пропор-циониро зиёд кунад;

(3) The quality of cement. For large plants’ new dry-process rotary kiln cement, the mixing ratio can be appropriately reduced, while for small plants, shaft kiln cement or cement with a large mixing ratio should be appropriately increased;

(4) Density and strength requirements of the product. Талаботи зичии паст ё қувваи баландтар бояд таносуби сементро зиёд кунад, талаботи зичии баланд ё қувваи пасттар метавонад таносуби сементро коҳиш диҳад;

(5) Initial growth temperature. Ҳарорати муолиҷаи ибтидоӣ пас аз рехтан (рехтан) пасттар аст (<25°C). The proportion of cement should be increased. When the initial curing temperature is high (25℃-45℃), the proportion of cement can be appropriately reduced. If steam curing or autoclave is used, it is still strong to reduce the proportion of cement;

(6) Variety and activity of active micro-aggregate (омехта). Истифодаи микроагрегатхои сер-фаъолият метавонад вазни киёсии цементро кам кунад (ба монанди шлаки ултра-нафс), хангоми истифода бурдани микроагрегатхои камфаъолият (монанди хокистари дуюмдараҷа) метавонад вазни киёсии цементро зиёд кунад.

Cie-China.org як провайдери пешбари иловаҳои бетонии кафк мебошад, ки агенти кафккунии бетонро таъмин мекунад, суперпластикизатор,мустаҳкамкунандаи қувваи бетони кафк барои бетони сабук, Блокҳои CLC. Агар шумо ҷустуҷӯ доред агенти кафккунанда, лутфан озод бошед бо мо тамос гиред.